BRAND NAME |
AI2O3 %
(min)
|
Fe2O3%
(max)
|
A.P.%
(min)
|
B.D.Gms/cc
(min)
|
C.C.S.
kgs/cm2
(min)
|
P.C.E.orton
(min) |
R.U.L.Ta°c
(min) |
P.L.C.%
(max)
|
|
ICI – 30 |
30 |
2.0 |
25 |
1.9 |
250 |
30 |
1300 |
+1.5 at
1350°C/2 hrs |
|
ICI - HHD |
35-37 |
2.1 |
25 |
2.0 |
300 |
30 |
1350 |
+0.75 at
1350°C/2 hrs |
|
ICI – 40 |
40 |
2.5 |
23 |
2.1 |
300 |
31 |
1400 |
+0.5 at
1400°C/2 hrs |
|
ICI – 45 |
45 |
2.6 |
22 |
2.2 |
350 |
32 |
1400 |
+0.8 at
1400°C/2 hrs |
|
ICI – 50 |
50 |
2.75 |
22 |
2.3 |
400 |
33 |
1420 |
+1.0 at
1450°C/2 hrs |
|
ICI – 60 |
60 |
3.0 |
20 |
2.5 |
450 |
34 |
1450 |
+1.5 at
1450°C/2 hrs |
|
ICI – 60 LF |
60 |
2.0 |
20 |
2.4 |
450 |
34 |
1450 |
+1.5 at
1450°C/2 hrs |
|
ICI – 70 |
70 |
3.2 |
18 |
2.65 |
550 |
36 |
1470 |
+1.5 at
1500°C/2 hrs |
|
ICI – 70 LF |
70 |
2.5 |
18 |
2.6 |
550 |
36 |
1470 |
+1.5 at
1500°C/2 hrs |
Note :
1.
Size Tolerance: ±1.5% or 2mm whichever is
greater
2. The above data is on basis of average results
MORTARS
|
Brand
Name |
Al203 |
Fe203 |
Grading (mm) |
Service Temperature ('C) |
Setting |
|
ICI - 30 M |
30 |
2.0 |
0-1 |
1300 |
Ceramic |
|
ICI - 40 M |
40 |
2.2 |
0-1 |
1350 |
Ceramic |
|
ICI - 50 M |
50 |
2.5 |
0-1 |
1400 |
Ceramic |
|
ICI - 60 M |
60 |
3.0 |
0-1 |
1450 |
Ceramic |
|
ICI - 70 M |
70 |
3.5 |
0-1 |
1500 |
Ceramic |
CATABLES
|
Brand
Name |
Al203
% (min) |
Fe203%
(max) |
C.C.S
(kgs/cm2)
at
110* C |
C.C.S
(kgs/cm2)
After firing |
MAX.
Service
Temp. (*C) |
|
ICI - 40 M |
40 |
2.0 |
250 |
350 |
1350 |
|
ICI - 60 M |
60 |
3.0 |
350 |
450 |
1450 |
|
ICI - 70 M |
70 |
3.5 |
400 |
500 |
1500 |
Note :
The above data is on basis of average results.